| Ablation behavior and mechanism of Cf/SiBCN composites in plasma ablation flame | |
| Ding, Q; Ni, DW; Jiang, YL; Chen, BW; Wang, Z; Kan, YM; Gao, L; Zhang, XY; Ding, YS; Dong, SM | |
| 2020-02-01 | |
| Source Publication | JOURNAL OF THE AMERICAN CERAMIC SOCIETY
 |
| ISSN | 0002-7820 |
| Issue | 2Pages:1321 |
| Subtype | Article |
| Abstract | In this work, Cf/SiBCN composites are fabricated by an improved precursor infiltration and pyrolysis (PIP) approach. Ablation behavior of the Cf/SiBCN composites is investigated in plasma ablation flame at a heat flux of 4.02 MW m(-2), which provides a quasi-real hypersonic service environment at a temperature up to 2200 degrees C. After ablation, the ablated surface is covered with oxidation products in the form of oxide layer, fibrous residues, or bubbles, which effectively isolates the sample surface from the plasma flame and inhibits the scouring of high-speed flame to the composites. As a result, the Cf/SiBCN composites present an excellent ablation-resistant property, with linear and mass recession rates as low as 0.0030 mm s(-1) and 0.0539 mg mm(-2) s(-1), respectively. It is also revealed that the material at ablation center undergoes crystallization and oxidation processes during ablation, while the ablation behavior at transition area and ablation fringe only contains oxidation process due to the local temperature difference. Si3N4 and SiC grains are precipitated from amorphous SiBCN matrix during the crystallization process, and the oxidation process mainly involves the oxidation of carbon fiber and SiBCN matrix, etc. |
| DOI | 10.1111/jace.16802 |
| WOS Keyword | HIGH-TEMPERATURE OXIDATION ; CERAMIC-MATRIX COMPOSITES ; C-F/SIBCN COMPOSITES ; PRECURSOR ; MICROSTRUCTURE ; RESISTANCE ; BORON ; KINETICS ; NITRIDE ; DESIGN |
| Language | 英语 |
| WOS Research Area | Materials Science |
| Publisher | WILEY |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.sic.ac.cn/handle/331005/28331 |
| Collection | 中国科学院上海硅酸盐研究所 |
| Recommended Citation GB/T 7714 | Ding, Q,Ni, DW,Jiang, YL,et al. Ablation behavior and mechanism of Cf/SiBCN composites in plasma ablation flame[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2020(2):1321. |
| APA | Ding, Q.,Ni, DW.,Jiang, YL.,Chen, BW.,Wang, Z.,...&Dong, SM.(2020).Ablation behavior and mechanism of Cf/SiBCN composites in plasma ablation flame.JOURNAL OF THE AMERICAN CERAMIC SOCIETY(2),1321. |
| MLA | Ding, Q,et al."Ablation behavior and mechanism of Cf/SiBCN composites in plasma ablation flame".JOURNAL OF THE AMERICAN CERAMIC SOCIETY .2(2020):1321. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment