Tribological properties and wear mechanisms of hot-pressed sintering mesocarbon microbeads (MCMBs)-SiC composites against different counterparts

doi:10.1016/j.ceramint.2019.10.116

SIC OpenIR

	Tribological properties and wear mechanisms of hot-pressed sintering mesocarbon microbeads (MCMBs)-SiC composites against different counterparts
	Wang, XJ; Yao, XM; Zhang, H; Liu, XJ; Huang, ZR
	2020-02-15
Source Publication	CERAMICS INTERNATIONAL
ISSN	0272-8842
Issue	3 Pages:3896
Subtype	Article
Abstract	The sliding tribological properties of dense MCMBs-SiC composites with 30 wt% MCMBs against self-mated counterparts, WC and SSiC were studied through a block-on-ring method under different loads respectively. The dense composites with excellent mechanical properties were fabricated through hot pressed sintering method. The results showed that the tribological properties of MCMBs-SiC composites were affected more by the properties of counterparts than the applied load. Under different loads, compared to WC-mated and SSiC-mated friction pairs, the self-mated pairs showed lower and more stable dry friction coefficient (mu) due to the lubricating film formed on the sliding surfaces. At the same time, the WC-mated friction pairs showed the lowest wear rate due to the highest fracture toughness of WC counterparts. The SSiC-mated friction pairs showed the highest p and wear rate under both applied loads. The wear mechanisms of different friction pairs were also investigated. The results showed that although the applied loads and counterparts were different, the wear mechanisms of each friction pair can be divided into three stages. For WC-mated and SSiC-mated friction pairs, wear mechanisms were almost the same. The first stage was the mechanical wear of grains, then following by tribochemical reactions (mostly oxide reactions) and finally removal of tribochemical layers. For self-mated friction pairs, during the third stage, the lubricating films was generated on the working surfaces due to a large amount of graphite phase from MCMBs in the composites.
DOI	10.1016/j.ceramint.2019.10.116
WOS Keyword	C/C-SIC COMPOSITES ; SILICON-CARBIDE ; FRICTION ; BEHAVIOR ; CERAMICS
Language	英语
WOS Research Area	Materials Science
Publisher	ELSEVIER SCI LTD
Citation statistics	Cited Times:1[WOS] [WOS Record] [Related Records in WOS]
Document Type	期刊论文
Identifier	http://ir.sic.ac.cn/handle/331005/28302
Collection	中国科学院上海硅酸盐研究所
Recommended Citation GB/T 7714	Wang, XJ,Yao, XM,Zhang, H,et al. Tribological properties and wear mechanisms of hot-pressed sintering mesocarbon microbeads (MCMBs)-SiC composites against different counterparts[J]. CERAMICS INTERNATIONAL,2020(3):3896.
APA	Wang, XJ,Yao, XM,Zhang, H,Liu, XJ,&Huang, ZR.(2020).Tribological properties and wear mechanisms of hot-pressed sintering mesocarbon microbeads (MCMBs)-SiC composites against different counterparts.CERAMICS INTERNATIONAL(3),3896.
MLA	Wang, XJ,et al."Tribological properties and wear mechanisms of hot-pressed sintering mesocarbon microbeads (MCMBs)-SiC composites against different counterparts".CERAMICS INTERNATIONAL .3(2020):3896.

Files in This Item:
There are no files associated with this item.

If you have any objections to this item, please fill out the form below and the administrator will contact you as soon as possible.
Content:
Email：	*
Institution:
Verification Code:	Refresh

Any comments and suggestions are welcomed.
Title:	*
Content:
Email：	*
Verification Code:	Refresh

中国科学院上海硅酸盐研究所机构知识库