Fabrication of Nd:YAG transparent ceramics from co-precipitated powders by vacuum pre-sintering and HIP post-treatment

doi:10.1016/j.optmat.2020.109728

SIC OpenIR

	Fabrication of Nd:YAG transparent ceramics from co-precipitated powders by vacuum pre-sintering and HIP post-treatment
	Tian, F; Chen, C; Liu, Y; Liu, Q; Ivanov, M; Wang, QQ; Jiang, N; Chen, HH; Yang, ZX; Xie, TF; Li, J
	2020-03-01
Source Publication	OPTICAL MATERIALS
ISSN	0925-3467
Subtype	Article; Proceedings Paper
Abstract	Using the nanopowders made by a reverse co-precipitation as raw materials, neodymium doped yttrium aluminum garnet (Nd:YAG) transparent ceramics were fabricated by vacuum pre-sintering with subsequent hot isostatic pressing (HIP) post-treatment. The green bodies were pre-sintered in vacuum at 1450 degrees C-1800 degrees C for 2 h and then HIPed at 1750 degrees C for 3 h under 200 MPa Ar atmosphere. Densification behavior and microstructure of the Nd:YAG ceramics before and after the HIP-treatment were investigated. Influences of the annealing temperature on transmittance and microstructure of the Nd:YAG ceramics were also studied. The ceramics presintered at 1750 degrees C for 2 h and post-HIPed at 1750 degrees C for 3 h without any additional annealing in air were shown to have the best in-line transmittance of 79.1% at 1064 nm.
DOI	10.1016/j.optmat.2020.109728
WOS Keyword	OPTICAL-PROPERTIES ; MICROSTRUCTURE DEVELOPMENT ; DENSIFICATION ; NANOPOWDERS
Language	英语
WOS Research Area	Materials Science ; Optics
Publisher	ELSEVIER
Citation statistics	Cited Times:3[WOS] [WOS Record] [Related Records in WOS]
Document Type	期刊论文
Identifier	http://ir.sic.ac.cn/handle/331005/28244
Collection	中国科学院上海硅酸盐研究所
Recommended Citation GB/T 7714	Tian, F,Chen, C,Liu, Y,et al. Fabrication of Nd:YAG transparent ceramics from co-precipitated powders by vacuum pre-sintering and HIP post-treatment[J]. OPTICAL MATERIALS,2020.
APA	Tian, F.,Chen, C.,Liu, Y.,Liu, Q.,Ivanov, M.,...&Li, J.(2020).Fabrication of Nd:YAG transparent ceramics from co-precipitated powders by vacuum pre-sintering and HIP post-treatment.OPTICAL MATERIALS.
MLA	Tian, F,et al."Fabrication of Nd:YAG transparent ceramics from co-precipitated powders by vacuum pre-sintering and HIP post-treatment".OPTICAL MATERIALS (2020).

Files in This Item:
There are no files associated with this item.

If you have any objections to this item, please fill out the form below and the administrator will contact you as soon as possible.
Content:
Email：	*
Institution:
Verification Code:	Refresh

Any comments and suggestions are welcomed.
Title:	*
Content:
Email：	*
Verification Code:	Refresh

中国科学院上海硅酸盐研究所机构知识库