Microstructure and properties of MgAl2O4 transparent ceramics fabricated by hot isostatic pressing
Liu, Q; Jing, YQ; Su, S; Li, XY; Liu, X; Feng, YG; Chen, XP; Li, J
2020-06-01
Source PublicationOPTICAL MATERIALS
ISSN0925-3467
SubtypeArticle
AbstractTransparent magnesium aluminate spinet (MgAl2O4) ceramics were successfully fabricated by presintering in air and hot isostatic pressing (HIP) with commercial spinet and calcium oxide powders as raw materials. Due to the liquid phase formation of calcium aluminate in the presintering process, small amount of CaO (0.1 wt%) is found to be very effective for the densification of the ceramics. The influence of presintering temperature on the microstructure, densification process, optical quality and mechanical properties of MgAl2O4 ceramics were investigated. It is found that the relative density of presintered MgAl2O4 ceramics changes from 86.3% to 99.4% when the presintering temperature increases from 1450 degrees C to 1550 degrees C. The average grain size of MgAl2O4 ceramics increases from 0.7 mu m to 4.5 mu m with the increase of presintering temperature from 1450 to 1650 degrees C. The transparent MgAl2O4 ceramic sample presintered at 1525 degrees C for 3 h and HIP post-treated at 1600 degrees C for 3 h shows high in-line transmittances of 86.3% at 1100 nm and 82.5% at 600 nm, the average grain size of 1.5 mu m, the high flexural strength of 281 +/- 16 MPa and hardness of 13.23 +/- 0.07 GPa.
DOI10.1016/j.optmat.2020.109938
WOS KeywordMAGNESIUM-ALUMINATE SPINEL ; PLASMA SINTERING SPS ; OPTICAL-PROPERTIES ; FRACTURE-TOUGHNESS ; QUALITY ; PERFORMANCE ; NANOPOWDERS
Language英语
WOS Research AreaMaterials Science ; Optics
PublisherELSEVIER
Citation statistics
Document Type期刊论文
Identifierhttp://ir.sic.ac.cn/handle/331005/28015
Collection中国科学院上海硅酸盐研究所
Recommended Citation
GB/T 7714
Liu, Q,Jing, YQ,Su, S,et al. Microstructure and properties of MgAl2O4 transparent ceramics fabricated by hot isostatic pressing[J]. OPTICAL MATERIALS,2020.
APA Liu, Q.,Jing, YQ.,Su, S.,Li, XY.,Liu, X.,...&Li, J.(2020).Microstructure and properties of MgAl2O4 transparent ceramics fabricated by hot isostatic pressing.OPTICAL MATERIALS.
MLA Liu, Q,et al."Microstructure and properties of MgAl2O4 transparent ceramics fabricated by hot isostatic pressing".OPTICAL MATERIALS (2020).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Liu, Q]'s Articles
[Jing, YQ]'s Articles
[Su, S]'s Articles
Baidu academic
Similar articles in Baidu academic
[Liu, Q]'s Articles
[Jing, YQ]'s Articles
[Su, S]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Liu, Q]'s Articles
[Jing, YQ]'s Articles
[Su, S]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.