Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing
Lu, H; Liu, P; Tao, XH; Wang, J; Jiang, ZS; Zhang, J; Xu, XD; Tang, DY
2020-10-01
Source PublicationOPTICAL MATERIALS
ISSN0925-3467
SubtypeArticle
AbstractMid-infrared ZnSe0.9S0.1 transparent mixed crystal ceramics were successfully fabricated by hot pressing (HP) in combination with post hot isostatic pressing (HIP). The phase structure of the as-fabricated mixed ceramics was found to be composed of cubic sphalerite, and the existence of any secondary phase was not detected. It was noticed that after post HIP treatment, the grain size increased greatly, and many closed pores in the samples disappeared. The specimens HP sintered at 1000 degrees C under 60 MPa and post HIP treated at 1300 degrees C under 196 MPa in the Ar atmosphere for six hours had the best transmission of 62.3% at 14 mu m.
DOI10.1016/j.optmat.2020.110214
WOS KeywordZINC SELENIDE ; ZNS CERAMICS ; SULFIDE ; PHOTOLUMINESCENCE
Language英语
WOS Research AreaMaterials Science ; Optics
PublisherELSEVIER
Citation statistics
Document Type期刊论文
Identifierhttp://ir.sic.ac.cn/handle/331005/27705
Collection中国科学院上海硅酸盐研究所
Recommended Citation
GB/T 7714
Lu, H,Liu, P,Tao, XH,et al. Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing[J]. OPTICAL MATERIALS,2020.
APA Lu, H.,Liu, P.,Tao, XH.,Wang, J.,Jiang, ZS.,...&Tang, DY.(2020).Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing.OPTICAL MATERIALS.
MLA Lu, H,et al."Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing".OPTICAL MATERIALS (2020).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Lu, H]'s Articles
[Liu, P]'s Articles
[Tao, XH]'s Articles
Baidu academic
Similar articles in Baidu academic
[Lu, H]'s Articles
[Liu, P]'s Articles
[Tao, XH]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Lu, H]'s Articles
[Liu, P]'s Articles
[Tao, XH]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.