| Fabrication, microstructures, and optical properties of Yb:Lu2O3 laser ceramics from co-precipitated nano-powders | |
| Liu, ZY; Toci, G; Pirri, A; Patrizi, B; Feng, YG; Wei, JB; Wu, F; Yang, ZX; Vannini, M; Li, J | |
| 2020-11-07 | |
| Source Publication | JOURNAL OF ADVANCED CERAMICS
 |
| ISSN | 2226-4108 |
| Subtype | Article; Early Access |
| Abstract | The Yb:Lu2O3 precursor made up of spherical particles was synthesized through the co-precipitation method in the water/ethanol solvent. The 5 at% Yb:Lu2O3 powder is in the cubic phase after calcination at 1100 degrees C for 4 h. The powder also consists of spherical nanoparticles with the average particle and grain sizes of 96 and 49 nm, respectively. The average grain size of the pre-sintered ceramic sample is 526 nm and that of the sample by hot isostatic pressing grows to 612 nm. The 1.0 mm-thick sample has an in-line transmittance of 81.6% (theoretical value of 82.2%) at 1100 nm. The largest absorption cross-section at 976 nm is 0.96x10(-20) cm(2) with the emission cross-section at 1033 nm of 0.92x10(-20) cm(2) and the gain cross sections are calculated with the smallest population inversion parameter beta of 0.059. The highest slope efficiency of 68.7% with the optical efficiency of 65.1% is obtained at 1033.3 nm in quasi-continuous wave (QCW) pumping. In the case of continuous wave (CW) pumping, the highest slope efficiency is 61.0% with the optical efficiency of 54.1%. The obtained laser performance indicates that Yb:Lu2O3 ceramics have excellent resistance to thermal load stresses, which shows great potential in high-power solid-state laser applications. |
| DOI | 10.1007/s40145-020-0403-8 |
| WOS Keyword | YBSC2O3 TRANSPARENT CERAMICS ; SPECTROSCOPIC PROPERTIES ; SOLID-SOLUTIONS ; LU2O3 ; NANOPOWDERS ; OSCILLATION ; SESQUIOXIDE ; CRYSTAL ; MODEL |
| Language | 英语 |
| WOS Research Area | Materials Science |
| Publisher | SPRINGER |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.sic.ac.cn/handle/331005/27634 |
| Collection | 中国科学院上海硅酸盐研究所 |
| Recommended Citation GB/T 7714 | Liu, ZY,Toci, G,Pirri, A,et al. Fabrication, microstructures, and optical properties of Yb:Lu2O3 laser ceramics from co-precipitated nano-powders[J]. JOURNAL OF ADVANCED CERAMICS,2020. |
| APA | Liu, ZY.,Toci, G.,Pirri, A.,Patrizi, B.,Feng, YG.,...&Li, J.(2020).Fabrication, microstructures, and optical properties of Yb:Lu2O3 laser ceramics from co-precipitated nano-powders.JOURNAL OF ADVANCED CERAMICS. |
| MLA | Liu, ZY,et al."Fabrication, microstructures, and optical properties of Yb:Lu2O3 laser ceramics from co-precipitated nano-powders".JOURNAL OF ADVANCED CERAMICS (2020). |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment