Strong ZrC ceramics at high temperatures with the addition of W
Shen, Yi-Bo; Wang, Xin-Gang; Zhang, Guo-Jun; Xue, Jia-Xiang; Li, Qiang; Jiang, Dan-Yu
2019-06-01
Source PublicationJOURNAL OF THE AMERICAN CERAMIC SOCIETY
ISSN0002-7820
Volume102Issue:6Pages:3090
SubtypeArticle
AbstractThe effect of W addition on densification, microstructure, and mechanical properties of ZrC ceramics was investigated. W reacted with carbon in ZrC to form WC, which resulted in the formation of ZrC1-x at 1300-1700 degrees C, while WC was further dissolved in ZrC to form a (Zr1-yWy)C1-x solid solution at 1800-2000 degrees C. The relative density of ZrC with 5mol% W (ZW5, 96.8%) was markedly higher than that of pure ZrC (Z0, 94.8%). ZW5 exhibited a fine homogeneous microstructure with a grain size (2.6 +/- 0.5m) much smaller than that of Z0 (10.9 +/- 3.0m), while excess W addition (10mol%) in ZrC adversely affected the densification and the microstructure. The flexure strength of Z0 was 446 +/- 46MPa at room temperature, which almost linearly decreased to 281 +/- 10MPa at 1800 degrees C in a high-purity flowing argon atmosphere. The flexure strength of ZW5 was 512 +/- 40MPa at room temperature, and had no degradation even up to 1800 degrees C. The fine and homogeneous microstructure of ZW5 and the removal of oxygen impurity from the grain boundaries promoted the enhancement of high-temperature mechanical properties.
DOI10.1111/jace.16320
Language英语
WOS Research AreaMaterials Science
PublisherWILEY
Citation statistics
Document Type期刊论文
Identifierhttp://ir.sic.ac.cn/handle/331005/27087
Collection中国科学院上海硅酸盐研究所
Recommended Citation
GB/T 7714
Shen, Yi-Bo,Wang, Xin-Gang,Zhang, Guo-Jun,et al. Strong ZrC ceramics at high temperatures with the addition of W[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2019,102(6):3090.
APA Shen, Yi-Bo,Wang, Xin-Gang,Zhang, Guo-Jun,Xue, Jia-Xiang,Li, Qiang,&Jiang, Dan-Yu.(2019).Strong ZrC ceramics at high temperatures with the addition of W.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,102(6),3090.
MLA Shen, Yi-Bo,et al."Strong ZrC ceramics at high temperatures with the addition of W".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 102.6(2019):3090.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Shen, Yi-Bo]'s Articles
[Wang, Xin-Gang]'s Articles
[Zhang, Guo-Jun]'s Articles
Baidu academic
Similar articles in Baidu academic
[Shen, Yi-Bo]'s Articles
[Wang, Xin-Gang]'s Articles
[Zhang, Guo-Jun]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Shen, Yi-Bo]'s Articles
[Wang, Xin-Gang]'s Articles
[Zhang, Guo-Jun]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.