Fabrication and characterizations of 8.7 mol% Y2O3-ZrO2 transparent ceramics using co-precipitated nanopowders
Liu, Qiang; Chen, Penghui; Jiang, Nan; Zhang, Xing; Li, Xiaoying; Su, Sha; Hu, Zewang; Chen, Haohong; Xie, Tengfei; Li, Jiang
2019-10-01
Source PublicationSCRIPTA MATERIALIA
ISSN1359-6462
Volume171Pages:98
SubtypeArticle
Abstract8.7 mol% Y2O3-ZrO2 (Y0.16Zr0.84O1.92) precursor was synthesized by the co-precipitation method using ammonia as the precipitant. The Y0.16Zr0.84O1.92 powders calcined at 800 degrees C show a pure c-ZrO2 phase. The average crystallite size of the powders is 12.4 nm and weakly agglomerated to an average particle size of 15.5 nm. Y0.16Zr0.84O1.92 transparent ceramics were then successfully fabricated by pre-sintering at 1350 degrees C for 2 h and HIP post-treatment at 1750 degrees C for 1 h under 200 MPa without sintering additives. The in-line transmittance of Y0.16Zr0.84O1.92 ceramics (1 mm thick) exceeds 50.3% in the region of 400-850 nm, reaching about 65.3% at 800 nm. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
KeywordY2O3-ZrO2 Transparent ceramics Co-precipitation method HIP post-treatment
DOI10.1016/j.scriptamat.2019.06.029
Language英语
WOS Research AreaScience & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering
PublisherPERGAMON-ELSEVIER SCIENCE LTD
Citation statistics
Cited Times:4[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.sic.ac.cn/handle/331005/26808
Collection中国科学院上海硅酸盐研究所
Recommended Citation
GB/T 7714
Liu, Qiang,Chen, Penghui,Jiang, Nan,et al. Fabrication and characterizations of 8.7 mol% Y2O3-ZrO2 transparent ceramics using co-precipitated nanopowders[J]. SCRIPTA MATERIALIA,2019,171:98.
APA Liu, Qiang.,Chen, Penghui.,Jiang, Nan.,Zhang, Xing.,Li, Xiaoying.,...&Li, Jiang.(2019).Fabrication and characterizations of 8.7 mol% Y2O3-ZrO2 transparent ceramics using co-precipitated nanopowders.SCRIPTA MATERIALIA,171,98.
MLA Liu, Qiang,et al."Fabrication and characterizations of 8.7 mol% Y2O3-ZrO2 transparent ceramics using co-precipitated nanopowders".SCRIPTA MATERIALIA 171(2019):98.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Liu, Qiang]'s Articles
[Chen, Penghui]'s Articles
[Jiang, Nan]'s Articles
Baidu academic
Similar articles in Baidu academic
[Liu, Qiang]'s Articles
[Chen, Penghui]'s Articles
[Jiang, Nan]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Liu, Qiang]'s Articles
[Chen, Penghui]'s Articles
[Jiang, Nan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.