Effects of solid loading and calcination temperature on microstructure and properties of porous Si3N4 ceramics by aqueous gelcasting using DMAA system
Yin, Shuang; Jiang, Senchuan; Pan, Limei; Guo, Lin; Zhang, Zhenghao; Zhang, Jingxian; Li, Xiaoyun; Qiu, Tai; Yang, Jian
2019-11-01
Source PublicationCERAMICS INTERNATIONAL
ISSN0272-8842
Volume45Issue:16Pages:19925
SubtypeArticle
AbstractHerein, a low toxic N, N dimethylacrylamide (DMAA) system was used in preparation of porous Si3N4 ceramics by aqueous gelcasting, and variations in microstructure and properties with solid loading and calcination temperature were systematically investigated. In the considered solid loading range of 28-44 vol%, all the slurries exhibited superior rheological properties (<= 145 mPa.s at 95.40 s(-1) for 44 vol% solid loading) perfectly suitable for casting. With increasing solid loading, a decreased bulk density (1.71-1.69 g/cm(3)), volume shrinkage (37.73-13.77%) and flexural strength (46.56-26.75 MPa) of green bodies were obtained, exhibiting better mechanical properties than those derived from the conventional acrylamide (AM) system. Regarding Si3N4 ceramics with various solid loadings, the increase in calcination temperature favored the phase transformation alpha ->beta-Si3N4 and beta-Si3N4 growth, however, the increased solid loading exhibited an inhibiting effect on those since mass transport in gas phase was blocked due to the disruption of pore connectivity. The resulting microstructure changes imparted Si3N4 ceramics increasing flexural strength (110.36-367.88 MPa), fracture toughness (2.54-5.03 MPa.m(1/2)), as well as decreasing porosity (54.21-41.05%) and pore size (0.38-0.33 mu m). This work demonstrates the potential research value of DMAA system in preparing high performance porous Si3N4 ceramics through gelcasting technique.
KeywordSi3N4 ceramics Gelcasting Solid loading Calcination temperature Microstructure Mechanical properties
DOI10.1016/j.ceramint.2019.06.250
Language英语
WOS Research AreaMaterials Science
PublisherELSEVIER SCI LTD
Citation statistics
Document Type期刊论文
Identifierhttp://ir.sic.ac.cn/handle/331005/26741
Collection中国科学院上海硅酸盐研究所
Recommended Citation
GB/T 7714
Yin, Shuang,Jiang, Senchuan,Pan, Limei,et al. Effects of solid loading and calcination temperature on microstructure and properties of porous Si3N4 ceramics by aqueous gelcasting using DMAA system[J]. CERAMICS INTERNATIONAL,2019,45(16):19925.
APA Yin, Shuang.,Jiang, Senchuan.,Pan, Limei.,Guo, Lin.,Zhang, Zhenghao.,...&Yang, Jian.(2019).Effects of solid loading and calcination temperature on microstructure and properties of porous Si3N4 ceramics by aqueous gelcasting using DMAA system.CERAMICS INTERNATIONAL,45(16),19925.
MLA Yin, Shuang,et al."Effects of solid loading and calcination temperature on microstructure and properties of porous Si3N4 ceramics by aqueous gelcasting using DMAA system".CERAMICS INTERNATIONAL 45.16(2019):19925.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yin, Shuang]'s Articles
[Jiang, Senchuan]'s Articles
[Pan, Limei]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yin, Shuang]'s Articles
[Jiang, Senchuan]'s Articles
[Pan, Limei]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yin, Shuang]'s Articles
[Jiang, Senchuan]'s Articles
[Pan, Limei]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.