Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders
Liu, Qiang1; Dai, Zhengfa1,2; Hreniak, Dariusz3; Li, Shanshan2; Liu, Wenbin4; Wang, Wei2; Luo, Wei2; Li, Chaoyu2; Dai, Jiawei2; Chen, Haohong2; Kou, Huamin2; Shi, Yun2; Pan, Yubai5; Li, Jiang2
2017
发表期刊Optical Materials
ISSN09253467
卷号72页码:482-490
摘要Ytterbium doped scandium oxide (Yb:Sc2O3) nano-powders were synthesized by a co-precipitation method. Ammonium hydrogen carbonate (NH4HCO3) and ammonia sulfate ((NH4)2SO4) were used in the precipitation process as the precipitant and dispersing agent, respectively. Structural properties and morphology of the precursor and nano-powders were investigated by BET, XRD, and SEM measurements. Ultra-fine and low agglomerated 5 at%Yb:Sc2O3powders with the average particle size of 86 nm were obtained after calcination of the precipitate at 1100 °C for 5 h, that was found to be the optimal temperature for preparation of 5 at%Sc2O3powders for further sintering. 5 at%Yb:Sc2O3transparent ceramics with in-line transmittance of 73.9% at 1100 nm and average grain size of 182 μm were fabricated by vacuum sintering of the optimal powder at 1850 °C for 10 h. The microstructure, the spectroscopic properties and the gain characteristics of obtained 5 at%Yb:Sc2O3ceramics were also studied and discussed. © 2017
DOI10.1016/j.optmat.2017.05.057
EI入藏号20172703873026
EI主题词Ytterbium compounds
EI分类号802.3 Chemical Operations - 812.1 Ceramics
引用统计
文献类型期刊论文
条目标识符http://ir.sic.ac.cn/handle/331005/25945
专题中国科学院上海硅酸盐研究所
作者单位1.School of Material Science and Engineering, Jiangsu University, Zhenjiang; 212013, China;
2.Key Laboratory of Transparent and Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China;
3.Department of Excited State Spectroscopy, Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Wroclaw; 50-422, Poland;
4.Shanghai Key Laboratory of Crime Scene Evidence, Shanghai Research Institute of Criminal Science and Technology, Shanghai; 200083, China;
5.Department of Physics, Shanghai Normal University, Shanghai; 200234, China
推荐引用方式
GB/T 7714
Liu, Qiang,Dai, Zhengfa,Hreniak, Dariusz,et al. Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders[J]. Optical Materials,2017,72:482-490.
APA Liu, Qiang.,Dai, Zhengfa.,Hreniak, Dariusz.,Li, Shanshan.,Liu, Wenbin.,...&Li, Jiang.(2017).Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders.Optical Materials,72,482-490.
MLA Liu, Qiang,et al."Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders".Optical Materials 72(2017):482-490.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Liu, Qiang]的文章
[Dai, Zhengfa]的文章
[Hreniak, Dariusz]的文章
百度学术
百度学术中相似的文章
[Liu, Qiang]的文章
[Dai, Zhengfa]的文章
[Hreniak, Dariusz]的文章
必应学术
必应学术中相似的文章
[Liu, Qiang]的文章
[Dai, Zhengfa]的文章
[Hreniak, Dariusz]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。