Spark Plasma Sintering of Bioactive Ca2MgSi2O7Ceramics
Wang, Ming-Hui1; Zhong, Hong-Bin2; Fan, Yu-Chi3; Chen, Ting4
Source PublicationWuji Cailiao Xuebao/Journal of Inorganic Materials
AbstractThe bio-ceramics based on Ca and Si have wide development prospect in biomedical, which is attributed to their outstanding bioactivity and cytocompatibility. However, how to improve its sinterability is a key problem to be solved. In this study, pure Ca2MgSi2O7powders were prepared via a co-precipitation method, and then were sintering by spark plasma sintering (SPS) technique. The phase and the morphology of the resulting products were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The relative density and the bioactivity were also investigated by Archimedean method and simulated body fluid (SBF) soaking method, respectively. Experimental results showed that the Ca2MgSi2O7ceramics with density of about 99% could be achieved by spark plasma sintering at 1170 for 5 min under 70 MPa. After soaking in the simulated body fluid for 3 d, phosphate precipitation was observed on the surface of the ceramics, while bone-like hydroxyapatite was formed until 7 d soaking, indicating that the Ca2MgSi2O7ceramics prepared by SPS have good bioactivity to induce the sedimentation of bone-like hydroxyapatite. © 2017, Science Press. All right reserved.
EI Accession Number20174704417142
EI KeywordsSilicon compounds
EI Classification Number461.2 Biological Materials and Tissue Engineering - 461.6 Medicine and Pharmacology - 802.3 Chemical Operations - 804.2 Inorganic Compounds - 812.1 Ceramics
Citation statistics
Cited Times:3[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Affiliation1.Analysis and Testing Center, Donghua University, Shanghai; 201620, China;
2.School of Materials and Environmental Engineering, Hunan University of Humanities Science and Technology, Loudi; 417000, China;
3.Institute of Functional Materials, Donghua University, Shanghai; 201620, China;
4.Jingdezhen Ceramic Institute, Jingdezhen; 333001, China
Recommended Citation
GB/T 7714
Wang, Ming-Hui,Zhong, Hong-Bin,Fan, Yu-Chi,et al. Spark Plasma Sintering of Bioactive Ca2MgSi2O7Ceramics[J]. Wuji Cailiao Xuebao/Journal of Inorganic Materials,2017,32(8):825-830.
APA Wang, Ming-Hui,Zhong, Hong-Bin,Fan, Yu-Chi,&Chen, Ting.(2017).Spark Plasma Sintering of Bioactive Ca2MgSi2O7Ceramics.Wuji Cailiao Xuebao/Journal of Inorganic Materials,32(8),825-830.
MLA Wang, Ming-Hui,et al."Spark Plasma Sintering of Bioactive Ca2MgSi2O7Ceramics".Wuji Cailiao Xuebao/Journal of Inorganic Materials 32.8(2017):825-830.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, Ming-Hui]'s Articles
[Zhong, Hong-Bin]'s Articles
[Fan, Yu-Chi]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, Ming-Hui]'s Articles
[Zhong, Hong-Bin]'s Articles
[Fan, Yu-Chi]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, Ming-Hui]'s Articles
[Zhong, Hong-Bin]'s Articles
[Fan, Yu-Chi]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.