Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment
Jiang, Nan1,2; Liu, Qiang2; Xie, Tengfei1; Ma, Peng1; Kou, Huamin1; Pan, Yubai3; Li, Jiang1
2017
Source PublicationJournal of the European Ceramic Society
ISSN09552219
Volume37Issue:13Pages:4213-4216
AbstractHighly transparent aluminum oxynitride (AlON) ceramics were fabricated by pressureless sintering with hot isostatic pressing (HIP) post-treatment. The experimental results showed that the optical transparency of AlON ceramics was improved markedly over the visible and near-infrared range by HIP at 1825 °C for 3 h in 200 MPa argon gas, which derived from the elimination of residual pores in the prepared ceramics. For AlON ceramics pre-sintered at 1800 °C, the transmittances of the sample increased from 63.6% to 84.8% at 600 nm and from 75.4% to 86.1% at 2000 nm, respectively. The average grain size of the HIPed sample was about 47.9 μm. © 2017 Elsevier Ltd
DOI10.1016/j.jeurceramsoc.2017.04.028
EI Accession Number20171903640974
EI KeywordsNitrogen compounds
EI Classification Number741.1 Light/Optics - 812.1 Ceramics - 951 Materials Science
Citation statistics
Cited Times:7[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.sic.ac.cn/handle/331005/25499
Collection中国科学院上海硅酸盐研究所
Affiliation1.Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China;
2.School of Materials Science and Engineering, Jiangsu University, Zhenjiang; Jiangsu; 212013, China;
3.Shanghai Normal University, Shanghai; 200234, China
Recommended Citation
GB/T 7714
Jiang, Nan,Liu, Qiang,Xie, Tengfei,et al. Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment[J]. Journal of the European Ceramic Society,2017,37(13):4213-4216.
APA Jiang, Nan.,Liu, Qiang.,Xie, Tengfei.,Ma, Peng.,Kou, Huamin.,...&Li, Jiang.(2017).Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment.Journal of the European Ceramic Society,37(13),4213-4216.
MLA Jiang, Nan,et al."Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment".Journal of the European Ceramic Society 37.13(2017):4213-4216.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Jiang, Nan]'s Articles
[Liu, Qiang]'s Articles
[Xie, Tengfei]'s Articles
Baidu academic
Similar articles in Baidu academic
[Jiang, Nan]'s Articles
[Liu, Qiang]'s Articles
[Xie, Tengfei]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Jiang, Nan]'s Articles
[Liu, Qiang]'s Articles
[Xie, Tengfei]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.